Luvocom 1/CF/20/HS Polyamide 66 PA66 CF12 Carbon Fiber Filled Nylon 66 Sheet

• Customization: Available
• Material: PA
• Kind: Nylon Plastic
• Model NO.: MBH-PA66CF12S-040
• Water Absorption: 1.5%~3.5%
• Contraction Percentage: 2.0%~5.0%
• Tensile Strength: 30~40MPa
• Color: Nature
• Size: W 630*T50*1000mm or Customized Thickness and Lengt
• Machining Service: Yes
• Advantage: Purified for Medical Use and Clean Use
• Modified Service: Yes
• Application Filed: Medical Pharmacy / Water Treatment / Semiconductor
• Transport Package: as Per Customer's Request
• Specification: as per customer's request
• Trademark: MBH
• Origin: China
• HS Code: 3926909090
• Production Capacity: 500000 Sets Per Year
• Package Size: 10.00cm * 70.00cm * 45.00cm
• Package Gross Weight: 9.000kg

Product Description

PA66 CF12

Detailed Photos

PA66 GF sheet

PURE PA66 Nylon 66 Sheet, width 630,  Length and Thickness Customized support



PURE PA66 +GF30 Sheet, width 630,  Length and Thickness Customized support

Product Description

TDS  LUVOCOM 1/CF/20/HS - PA66-CF - LEHVOSS Group
 

Physical	Nominal Value	Unit	Test Method
Density	1.23	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	14000	MPa	ISO 527-2
Tensile Stress (Break)	210	MPa	ISO 527-2
Tensile Strain (Yield)	3.0	%	ISO 527-2
Flexural Modulus	12000	MPa	ISO 178
Flexural Stress	315	MPa	ISO 178
Coefficient of Friction
Dynamic	0.22
Static	0.17
Flexural Strain at Flexural Strength	3.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	160	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	15	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1fU
-30°C	40	kJ/m²	ISO 179/1fU
23°C	45	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	120	°C	UL 746B
Vicat Softening Temperature	254	°C	ISO 306/A
CLTE - Flow	1.8E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.43	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+3	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	75.0	°C
Vacuum dryer, B	105	°C
Drying Time
Hot air dryer, A	6.0 - 16	hr
Vacuum dryer, B	4.0 - 6.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	290 - 310	°C
Middle Temperature	290 - 310	°C
Front Temperature	290 - 310	°C
Nozzle Temperature	280 - 300	°C
Processing (Melt) Temp	290	°C
Mold Temperature	90.0 - 120	°C

 

 

 

 

 

Material	Brand	Size (Rod)	Services	Application
PA66+CF12	MBH	T 5 10 20 30 35 40 50 60 70 80 90 100 or customized	sheet/rod/profile extrusion and machining	sliding/wear/bearing area

Ningbo MBH, Founded in 2012, with its headquarters in Stuttgart, Germany, is a supplier of special engineering plastic application solutions in Ningbo, including all kinds of customized plastic extrusion and parts CNC machining.

we have for example extruded PEEK, PFA, PEI, PVDF, PCTFE, POM etc, or we could help modify the materials as your requested. our production and processing department has accumulated years of experience, providing comprehensive product design, processing, installation, and usage consultation to global customers.

 

Material Including:
High-Temperature resistance Material:
PBI,PEEK,PI,PAI,PEI,PPSU,PES,PSU,PPS,LCP etc.
Engineer Plastic:
POM,PA,PPA,UPE,POK,PPO etc.
All series of Fluoropolymer Thermoplastic:
PTFE,PVDF,PFA,ECFTE,PCTFE,ETFE,FEP etc.
Elastomeric Material:
TPU (moulding concreted), TPU(thermoplasticity), TPEE etc.
Other specific special functional Material:
TPX,COP,COC etc.
Other customizable modified Material by filling aramid fiber, carbon fiber, carbon nano-tube, PBO, molybdenum disulfide, PTFE, mineral, glass fiber, ceramic, boron nitride, silicon nitride etc.