Customerizd High Performance Peek CF30 Ca30 Solid Rods

• Customization: Available
• Material: Peek
• Kind: Hard Plastic Rods
• Model NO.: MBH-PEEKCFR-070
• Water Absorption: ＜0.01%
• Contraction Percentage: 0.4%~1.4%
• Tensile Strength: 81~130MPa
• Color: Nature Beige
• Size: Max 260mm Dia. Per Customized
• Machining Service: Yes
• Advantage: High Performance
• Modified Service: Yes
• Application Filed: Medical / E/E / Semiconductor / Aerospace etc
• Transport Package: as Per Customer′s Request
• Specification: as per customer′s request
• Trademark: MBH
• Origin: China
• HS Code: 3926909090
• Production Capacity: 500000 Sets Per Year

Product Description

Product Description

 

Customerizd high performance PEEK CF30 CA30 solid Rods

Material	Brand	Size (Rod)	Services	Application
PEEK	MBH	Dia. 4 /5/6/7/8/9/10/13/16/18/22/ 25/26/40/45/50/55/60/65/70/75 /80/85/90/100/130/160mm or customized Thickness 5mm-100mm sheet	sheet/rod extrusion and machining and plastic modified services	medical, pharmaceutical, and semi-conductor, Aerospace, Auto etc.

 

Ketron® GF30 Polyetheretherketone PEEK is a 30% glass fiber reinforced grade with excellent dimensional stability and outstanding chemical, corrosion, and creep resistance. With the addition of glass fibers, Ketron® GF30 PEEK has a significantly low expansion rate and high flexural modulus. In addition to these cPEEK CF 30 is a 30% carbon filled PEEK material that is manufactured by Ensinger under the tradename TECAPEEK CF30 black. Its carbon fibre reinforcement lends the material a high level of rigidity and creep strength. Carbon fibre reinforced PEEK demonstrates very high mechanical strength values, while exhibiting lower density than 30% glass fibre filled peek. Furthermore, carbon fibre composites tend to be less abrasive than glass fibres while simultaneously resulting in improved wear and friction properties. The addition of carbon fibres also ensures a significantly higher level of heat conductivity which is also beneficial for increasing part life in sliding applications. Carbon filled PEEK has also an excellent resistance to hydrolysis in boiling water and superheated steam.

Typical Properties		Test standard	Unit	Value
Physical
Colour				black
Density		ISO 1183-1	g/cm3	1.40
Water Aborption	23ºC, 50%RH	ISO 62	-	0.16
Thermal
Thermal conductivity at 23ºC		ISO 11359	10^-5/K	10.00
Max. material working Temperature(Rti)		UL 746B	ºC	240.00
Melting point Tm		DSC	ºC	343.00
Glass transition temperature Tg		DSC	ºC	143.00
Form stability  Tm.HDT/ A1.8 Mpa		Din EN ISO 75	ºC	336.00
Mechnical
tension Test	Tensile Strength at break	DIN EN ISO 527	MPa	260.00
	elongation at break	DIN EN ISO 527	%	1.70
	bending strength	DIN EN ISO 178	MPa	380.00
Compressive strength		DIN EN ISO 604	MPa	250.00
Charpy Impact Strength (no notch)		EN ISO 179	kJ/m^2	45.00
Charpy Impact Strength (with notch)		EN ISO 179	kJ/m^2	7.00
shore Hardness		ISO 868	Scale D	88.00
Electrical
Electrical Resistivity		DSC	j/(kg*K)	1800
PV value at V=0.5 m/s(30 m/min)		IEC 60093	Ω*cm	1.0E5
others

 

 